Kingroon Pink PLA compatible for most FDM 3D printers:
| PLA Nozzle Temp | 220±10°C |
| PLA Bed Temp | 25°C - 60°C |
| Printing Speed | 40-80mm/s |
| Density (g/cm³) | 1.17-1.24(g/cm³ at 21.5°C) |
| Retraction Distance | 1mm |
| Retraction Speed | 20mm/s |
| Glass transition temperature | 60-65°C |
| Tensile strenghth (X-Y) | 28.1±1.3 MPa |
| Bending strength | 48±1.9 MPa |
Specifications:
Material: PLA
Color: Pink
Diameter: 1.75mm
Weight: 1kg / pack
Spool size: φ200*64mm (φ8.87*2.5in) / Inside Diameter: 60mm (2.36in)
Package includes:
Pink PLA 1kg * 2 pack
With / Without filament dryer box * 1 set
Shipping based on the local warehouse coverage, inventory and the product you ordered. For more details please check: https://kingroon.com/pages/shipping-policyAll returns or exchanges must be made within 15 days of the date of purchase as specified on your proof of purchase. If you received wrong or defective products, you must submit a return request within 3 days after the delivery(included the delivery day). For more details, please check: https://kingroon.com/pages/kingroon-official-eshop-warranty-return-policy
Recently Viewed Products
| PLA | PETG | Rapid PLA | |
|---|---|---|---|
| RECOMMENDED EXTRUSION/NOZZLE TEMP: | 190°C - 220°C（recommended 205°C） | 220-260°C（recommended 220°C） | 200-230°C（recommended 220°C） |
| RECOMMENDED HEATED BED TEMP: | 50-65°C | 80-80°C | 40-60°C |
| PRINTING SPEED: | 30~70mm/s | 30~600 mm/s | 30~600 mm/s |
| PRINT LAYER THICKNESS: | 0.2mm | 0.2mm | 0.2mm |
| RECOMMENDED PLATFORM: | Glass/Fiberglass Board/PVP glue stick or textured paper | Glass/Fiberglass Board/PEI+PVP glue stick or platform spray | Glass/Fiberglass Board/PEI+PVP glue stick or platform spray |
| DIMENSIONAL ACCURACY 99% PROBABILITY: | +/- 0.02mm | +/- 0.02 mm | +/- 0.02 mm |
| NET WEIGHT: | 1 kg/spool (2.2 lbs) | 1 kg/spool (2.2 lbs) | 1 kg/spool (2.2 lbs) |
| DENSITY: | 1.2（g/cm³） | 1.27（g/cm³） | 1.2（g/cm³） |
| TENSILE STRENGTH (X-Y) : | ≥ 50（MPa） | ≥60（MPa） | ≥60（MPa） |
| ELONGATION AT BREAK (X-Y) : | 11.2 (%) | 19 (%) | 19 (%) |
| BENDING MODULUS : | 1913（MPa） | 2680（MPa） | 2680（MPa） |
| BENDING STRENGTH : | 91（MPa） | 80（MPa） | 80（MPa） |
| CHARPY IMPACT STRENGTH : | 5.4（kJ/m²） | 3.85 (KJ/m²) | 3.85 (KJ/m²) |
| MELT INDEX: | 14(190℃/2.16kg)g/10min | 8.2(190°C/2.16kg)g/10min | 8.2(190°C/2.16kg)g/10min |
| THERMAL DISTORTION TEMP: | 53°C (0.45MPa) | 53°C (0.45MPa) | 53°C (0.45MPa) |
| FAN: | 100% | 100% | 100% |
| ROCKWELL HARDNESS: | 88 | 88 | 88 |